Analysis of the damage evolution in steel specimens under tension by means of XRCT
Año:2017
Áreas de investigación
  • Caracteristicas de los materiales,
  • Ingeniería de construcción
Datos
Descripción
When a steel specimen is tested under tension, damage usually develops evenly all along the specimen, finally necking and leading to the typical cup-cone fracture surface. Nevertheless, some steels present an unusual fracture pattern consisting on a plane fracture surface with a dark region in the centre of the fracture zone. In this contribution, the authors analyse the evolution of the internal damage by using X-ray computed tomography (XRCT) on 3mm-diametre specimens of two steels. The specimens are tested in subsequent loading steps, after each of which it is unloaded and analysed with XRCT. This procedure helps to identify the evolution of damage developed inside each specimen at predefined strain levels. XRCT reveals a very high initial porosity in the material with the cup-cone fracture pattern and a very low initial porosity in the other. In the latter, fracture is triggered by a concentrated internal damage that can be seen as an internal notch which produces a stress concentration that leads to the eventual failure.
Internacional
Si
Nombre congreso
International Symposium on Notch Fracture
Tipo de participación
960
Lugar del congreso
Revisores
Si
ISBN o ISSN
978-84-617-9463-8
DOI
Fecha inicio congreso
29/03/2017
Fecha fin congreso
31/03/2017
Desde la página
88
Hasta la página
93
Título de las actas
Proceedings of the International Symposium on Notch Fracture
Esta actividad pertenece a memorias de investigación
Participantes
Grupos de investigación, Departamentos, Centros e Institutos de I+D+i relacionados
  • Creador: Grupo de Investigación: Materiales Estructurales Avanzados y Nanomateriales
  • Centro o Instituto I+D+i: CENTRO INVEST. MATERIALES ESTRUCTURALES (CIME)
  • Centro o Instituto I+D+i: Centro de tecnología Biomédica CTB
  • Grupo de Investigación: Tecnología de la Construcción y Ciencia de los Materiales para la edificación y la obra Civil
  • Departamento: Ciencia de Materiales
  • Departamento: Ingeniería Civil: Construcción